YTTRIA STABILIZED ZIRCONIA BEADS
  • ZrO2 : ≥ 94 %
  • Y2O3 : ≥ 5 %
  • Density : ≥ 6
  • Microhardness : 1200 ~ 1300 HV
  • Roundness : ≥ 95 %
  • Size (mm)
  • 0.1 0.2 0.3 0.4 0.5
    0.6 0.8 1.0 2.0 5.0
    Narrow size distribution / Smooth surface / 상기 외 다양한 size 가능
  • Application
    1. Dielectric materials, piezoelectric materials, capacitor
    2. Chemical materials, paint, pigment, printing ink, dye
    3. Advanced ceramic materials, frits and glazes
    4. Agrochemicals, cosmetics, pharmaceuticals
CERIA STABILIZED ZIRCONIA BEADS

  • ZrO2 + CeO2 : ≥ 95 %
  • Density : ≥ 6
  • Microhardness : 1200 HV
  • Size (mm)
  • 0.5 0.6 0.7 0.8 0.9
    1.0 5.0 10.0 15.0 20.0
    Narrow size distribution / Smooth surface / 상기 외 다양한 size 가능
  • Application
    1. 점성이 있는 제품의 공정에 적합 ( Paint, Ink 등 )
    2. 고속 / 미분쇄 공정
ZIRCONIUM SILICATE BEADS
  • ZrO2 : ≥ 52 %
  • SiO2 : 35 %
  • Al2O3 : 8 % 5 %
  • Roundness : ≥ 95 %
  • Size (mm)
  • 0.1 0.2 0.3 0.4 0.95
    0.6 0.8 1.0 2.0 5.0
    Narrow size distribution / Smooth surface / 상기 외 다양한 size 가능
  • Application
    1. Paints, inks and coatings
    2. Metal finishing and polishing
ALUMINA BEADS


  • Al2O3 : ≥ 90 %
  • Hardness (Mohs) : 9

  • Size (mm)
  • 0.5 0.6 0.7 0.8 1.0
    5.0 6.0 7.0 10 20

    상기 외 다양한 size 가능
GLASS BEADS


  • Density ( g/cm3) : 2.45
  • Hardness : 635
  • Color : Transparent

  • Size (mm)
  • 0.2 0.3 0.4 0.5 1.0
    1.5 2.0 2.5 3.0 2.0

    상기 외 다양한 size 가능